dc.description.abstractBu çalışmada, titrek kavak (Populus tremula L.) yongalarından üretilen kompozitlerdenlamine ağaç malzeme (Laminated Veneer Lumber: LVL), Paralel Strand Lumber (PSL) veLaminated Strand Lumber (LSL) kerestelerinin fiziksel ve mekanik özelliklerininbelirlenmesi amaçlanmıştır. Bu maksatla, kompozit kerestelere EN 310'a göre eğilme direncive eğilmede elastikiyet modülü, TS 2595'e göre liflere paralel yönde basınç direnci, TS2477'ye göre dinamik eğilme (şok) direnci, ASTM D 1037'ye göre liflere paralel çekme, EN319'a göre liflere dik çekme, ASTM D 1761'e göre vida tutma gücünün tayini, TS 2471'egöre rutubet tayini, TS 2472'e göre hacim yoğunluk belirleme testleri uygulanmıştır. Yapılantestler sonucunda en yüksek eğilme direnci LVL'de (64,51 N/mm2), en düşük kontrolörneklerinde (58,26N/mm2), elastikiyet modülü en yüksek LSL'de (8022,48 N/mm2), endüşük kontrol örneklerinde (7863,21N/mm2), liflere paralel basınç direnci en yüksek LVL'de(49,87 N/mm2), en düşük kontrol örneklerinde (33,63N/mm2), dinamik eğilme (şok) direncien yüksek PSL'de (0,50 kgm/cm2), en düşük masif kontrol örneğinde (0,34 kgm/cm2), liflereparalel çekme direnci değeri en yüksek LSL'de (26,04 N/mm2), en düşük kontrol örneklerinde(25,87 N/mm2), liflere dik çekme direnci en yüksek LVL'de (805,01 N/mm2), en düşükkontrol örneklerinde (757,34 N/mm2) bulunmuştur. Vida tutma kabiliyeti en yüksek LSL'de(8,44 N/mm2), en düşük kontrol örneklerinde (7,01 N/mm2), vida türüne göre en yüksek3,5x30'luk vidada (10,38 N/mm2), en düşük 17x17'lik vidada (5,59 N/mm2) tespit edilmiştir.Yoğunluk değeri en yüksek LSL'de (0,50 g/cm3), en düşük kontrol örneklerinde (0,34 g/cm3),rutubet değeri en yüksek masif kontrol örneğinde (% 11,51), en düşük PSL'de (% 8,00) eldeedilmiştir. Sonuç olarak; mobilya üretiminde ve inşaat sektöründe LVL'ye alternatif olarakPSL ve LSL'nin de kullanılması önerilebilir.
dc.description.abstractIn this study, it has been aimed to determine the physical and mechanical properties oflaminated wood material (Laminated Veneer Lumber: LVL), Paralel Strand Lumber (PSL)and Laminated Strand Lumber (LSL) timbers, produced from trembling poplar (Populustremula L.) strands. For this purpose, modulus of rupture (MOR) and modulus of elasticity(MOE) according to EN 310, compression strength parallel to grain according to TS 2595,dynamic bending (shock) strength in accordance with TS 2477, pulling in parallel directionwith fibers procedure of ASTM D 1037, pulling in vertical direction with fibers procedure ofEN 319, screw holding power procedure of ASTM D 1761, humidity according to TS 2471,density according to 2472 of timbers have been determined. As a result of the tests, thehighest MOR value vas obtained in LVL (65,51 N/ mm2), the lowest in control samples(58,26 N/ mm2), the highest MOE in LSL (8022,48 N/ mm2), the lowest in control samples(7863,21N/ mm2), the highest compression strength parallel to grain in LVL (49,87 N/ mm2),the lowest in control samples (33,63 N/ mm2), the highest dynamic bending (shock) strengthin PSL (0,50 kgm/cm2), the lowest in massive control samples (0,34 kgm/cm2), the highesttension strength in parallel direction with fibers in LSL (26,04 N/ mm2), the lowest in controlsamples (25,87 N/ mm2), the highest tension strength in vertical direction with fibers in LVL(805,01 N/ mm2), the lowest in control samples (757,34 N/ mm2). As for the screw holdingcapacity the highest value was observed in LSL (8,44 N/mm2), the lowest in control samples(7,01 N/ mm2), and procedure of the screw type, the highest value was observed in screw of3,5x30 (10,38N/mm2), the lowest was observed in screw of 17x17 (5,59 N/mm2). The highestdensity was observed in LSL (0,50 g/cm3), the lowest in control samples (0,34 g/cm3), thehighest humidity was observed in massive control samples (11,51%), the lowest in PSL (8,00%). In conclusion; it is advised the usage PSL and LSL as an alternative to LVL in furnitureproduction and building sector.en_US
dc.languageTurkish
dc.language.isotr
dc.rightsinfo:eu-repo/semantics/openAccess
dc.rightsAttribution 4.0 United Statestr_TR
dc.rights.urihttps://creativecommons.org/licenses/by/4.0/
dc.subjectAğaç İşleritr_TR
dc.subjectWood Productsen_US
dc.subjectTeknik Eğitimtr_TR
dc.subjectTechnical Educationen_US
dc.titleTitrek kavak yongalarından üretilen (lsl, lvl, psl) lamine ağaç malzemelerin direnç özelliklerinin belirlenmesi
dc.title.alternativeDetermination of some strength properties of laminated wood materials (lsl, lvl, psl) produced from poplar strands
dc.typemasterThesis
dc.date.updated2018-08-06
dc.contributor.departmentMobilya ve Dekorasyon Eğitimi Anabilim Dalı
dc.subject.ytmWoodworking
dc.subject.ytmWood materials
dc.subject.ytmPhysical properties
dc.subject.ytmPopulus
dc.subject.ytmDental veneers
dc.subject.ytmMechanical properties
dc.identifier.yokid315283
dc.publisher.instituteFen Bilimleri Enstitüsü
dc.publisher.universityKARABÜK ÜNİVERSİTESİ
dc.identifier.thesisid222071
dc.description.pages81
dc.publisher.disciplineDiğer


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record

info:eu-repo/semantics/openAccess
Except where otherwise noted, this item's license is described as info:eu-repo/semantics/openAccess