dc.description.abstractÖZETAmaç: Bu in vitro çalışmanın amacı, metal primerlerin, termal çevrimden sonra Kobalt-Krom alaşımı, Nikel-Krom alaşımı, Titanyum alaşımı ve ısı kür akrilik reçinesi arasındaki kesme bağ kuvvetine (SBS) etkisini değerlendirmektir.Gereç ve Yöntem: Kobalt-Krom, Titanyum (Ti90Al6V4) Nikel-Kromda 60 delikli mum örneği (çapta 10 mm ve kalınlık olarak 3 mm) dökülmüştür. Dökümden sonra, disk yüzeyleri, 110 um Alüminyum oksit ile 5 saniye boyunca kum püskürtülür. Her bir metalin numuneleri iki gruba ayrıldı (n = 20) ve aşağıdaki metal primerlerden birini aldı: (1) Alaşım Astar (Kuraray), (2) Z-Prime Plus (Bisco). Numuneler, kullanılan metal primerine göre 6 alt gruba ayrıldı (n = 10). Grup 1: Kobalt-Krom / Alaşımlı Astar, Grup 2: Kobalt-Krom / Z-Prime Plus, Grup 3: Titanyum / Alaşımlı Astar, Grup 4: Titanyum / Z-Prime Plus, Grup 5: Nikel-Krom / Alaşımlı Astar, Grup 6: Nikel-Krom / Z-Prime Plus. Tüm numuneler polimerizasyondan sonra 37 ° C'de damıtılmış suda 24 saat süreyle depolandı (5 ° C -55 ° C sıcaklıkta 5000 devir ve her sıcaklık için 30 saniyelik bekleme zamanı). Isıl çevrimden sonra numuneler, evrensel bir test makinesinde kesme modunda 0.5 mm / dak çapraz hızda test edildi. Veriler (MPa) tek yönlü ANOVA ve post Hoc Tukey (P <0.05) kullanılarak analiz edildi.Sonuç: Tek yönlü ANOVA, SBS değerlerinin kullanılan metal ve metal primer türüne göre değişiklik gösterdiğini ortaya koymuştur (P <0.05). En yüksek SBS, Grup 4 için kaydedildi: Titanyum / Z-Prime Plus (16.93 ± 3.3) MPa. En düşük SBS, Grup 5 için kaydedildi: Nikel-Krom / Alaşımlı Astar (1.20 ± 0.22).Metal türüne göre en yüksek SBS titanyum alaşımı (13, 18 ± 4, 59) MPa içindir. Ve metal astar için, Z-Prime Plus gruplarının (9.81 ± 6.75) MPa'nın kesilme yapışma mukavemeti, Alaşım astar gruplarının kayma bağ kuvvetine göre istatistiksel olarak daha yüksekti (p = 0.0001).Sonuç: Z-Prime Plus'ın kumlama sonrası kullanılmasının, ısıyla sertleşen akrilik protez bazlı reçinenin Titanyum alaşımına yapışmasını önemli ölçüde iyileştirdiği sonucuna varılabilir.Anahtar Kelimeler: makaslama mukavemeti, titanyum alaşımı, ısıl dolaşım, metal astar.
dc.description.abstractABSTRACTPurpose: The purpose of this in vitro study was to evaluate the effect of metal primers on the shear bond strength (SBS) between Cobalt-Chromium alloy, Nickel-Chromium alloy, Titanium alloy and heat cure acrylic resin after thermocycling.Material and Methods: Total number of60disc-shaped wax patterns (10mm in diameter and 3mm in thickness) were casted in Cobalt-Chromium, Titanium (Ti90Al6V4) Nickel-Chromium. After casting, the discs surface was sandblasted with110μm Aluminum oxide for 5 seconds. Specimens of each metal were divided into two groups (n=20) and received one of the following metal primers: (1) Alloy Primer (Kuraray), (2) Z-Prime Plus (Bisco). The specimens were divided into 6 subgroups (n=10) according to the metal primer used. Group1: Cobalt-Chromium / Alloy Primer, Group 2: Cobalt-Chromium / Z-Prime Plus, Group 3: Titanium / Alloy Primer, Group 4: Titanium / Z-Prime Plus, Group 5: Nickel-Chromium / Alloy Primer, Group 6: Nickel-Chromium / Z-Prime Plus. All the specimens were stored in the distilled water at 37℃ for 24 hours after polymerization we did thermocycle (5000 cycles at 5℃-55℃ with a 30- second dwell time for each temperature). After thermocycling, the specimens were tested in a universal testing machine at a crosshead speed of 0.5mm/min in shear mode. Data (MPa) were analyzed using one-way ANOVA and post Hoc Tukey (P< 0.05).Result: The one-way ANOVA indicated that SBS values varied according to type of metal and metal primer used (P< 0.05). The highest SBS was recorded for Group 4: Titanium / Z-Prime Plus (16.93±3.3) MPa. The lowest SBS was recorded for Group 5: Nickel-Chromium / Alloy Primer (1.20±0.22). According to the metal type the highest SBS was for Titanium alloy (13, 18±4, 59) MPa. And for the metal primer the shear bond strength of the Z- Prime Plus groups (9.81±6.75) MPa was statistically significant higher than the shear bond strength of Alloy primer groups (p=0.0001).Conclusion: It could be concluded that using Z- Prime Plus after sandblasting significantly improves the bonding of heat cured acrylic denture base resin to Titanium alloy.Keywords: shear bond strength, titanium alloy, thermocycling, metal primer.en_US
dc.languageEnglish
dc.language.isoen
dc.rightsinfo:eu-repo/semantics/openAccess
dc.rightsAttribution 4.0 United Statestr_TR
dc.rights.urihttps://creativecommons.org/licenses/by/4.0/
dc.subjectDiş Hekimliğitr_TR
dc.subjectDentistryen_US
dc.titleThe effect of different metal primers on shear bond strength between heat cure acrylic resin and different metal alloys after thermocycling
dc.typemasterThesis
dc.date.updated2019-03-07
dc.contributor.departmentDiş Hastalıkları ve Tedavisi Ana Bilim Dalı
dc.subject.ytmDental bonding
dc.subject.ytmDental materials
dc.subject.ytmDental cements
dc.subject.ytmAcrylic resins
dc.subject.ytmMetal alloys
dc.subject.ytmHeat change
dc.identifier.yokid10142309
dc.publisher.instituteSağlık Bilimleri Enstitüsü
dc.publisher.universityYENİ YÜZYIL ÜNİVERSİTESİ
dc.identifier.thesisid451313
dc.description.pages93
dc.publisher.disciplineDiğer


Files in this item

Thumbnail

This item appears in the following Collection(s)

Show simple item record

info:eu-repo/semantics/openAccess
Except where otherwise noted, this item's license is described as info:eu-repo/semantics/openAccess