Magnetic and microwave properties of Ba- and Sr- hexaferrites prepared by solid state reaction route with boron addition
dc.contributor.advisor | Baykal, Abdulhadi | |
dc.contributor.advisor | Sözeri, Hüseyin | |
dc.contributor.author | Mehmedi, Zulhice | |
dc.date.accessioned | 2021-05-07T11:37:53Z | |
dc.date.available | 2021-05-07T11:37:53Z | |
dc.date.submitted | 2015 | |
dc.date.issued | 2018-08-06 | |
dc.identifier.uri | https://acikbilim.yok.gov.tr/handle/20.500.12812/615559 | |
dc.description.abstract | Bu çalışmanın amacı bor katkısının M – tipi hekzaferitelerin (MFe12O19; M = Ba ve Sr) manyetik ve mikrodalga özelliklerine etkisini araştırmak. Numunelerin ferromanyetik rezonans frekanslarını değiştirmek amacıyla çeşitli divalent katyonlar (Mn+2, Zn+2, Co+2, Cu+2, Mg+2) hekzaferrit yapılara katkılandı. Hekzaferritelerin sentezi için katı hal sentez yöntemi kullanıldı. Sentez karışımına, düşük sıcaklıklarda kristal yapı oluşumunu desteklemek için %1 B2O3 eklendi. Numunelerin yapısal değişiklikleri XRD, SEM/TEM, FT-IR cihazlarıyla, manyetik özellikleri ise VSM cihazıyla ölçüldü. Mikrodalga yansıma / geçirgenlik ölçümleri netvörk analizör cihazıyla dalga klavuzu ya da koaksiyal hat yardımıyla 0 – 26 GHz frekans aralığında ölçüldü. Elektriksel ve manyetik geçirgenlik katsayılarının gerçel ve kompleks bileşenlerinin hesaplanması için NRW algoritması kullanıldı. Yansıma kayıpları standart formül kullanılarak hesaplandı. | |
dc.description.abstract | The aim of this research is to investigate effect of boron addition on magnetic and microwave properties of MFe12O19 (M=Ba, Sr) hexaferrites. Several diavalent cations (Mn+2, Zn+2, Co+2, Cu+2, Mg+2) were substituted to these hexaferrites to change ferromagnetic resonance frequency of the samples. Solid state reaction route was used during the study and 1 wt% B2O3 was added to initial mixture to improve the crystal growth at lower temperatures. Structural properties of the synthesized samples studied using XRD, SEM, FT-IR and magnetic properties determined using vibrating sample magnetometer. Microwave reflection/transmission measurements were done using network analyzer in waveguide or coaxial line in the frequency range of 0-26 GHz. NRW algorithm was used to obtain real and complex permeabilities and permittivities of samples. Then, reflection losses (RL) of samples were calculated using the standard formula. | en_US |
dc.language | English | |
dc.language.iso | en | |
dc.rights | info:eu-repo/semantics/openAccess | |
dc.rights | Attribution 4.0 United States | tr_TR |
dc.rights.uri | https://creativecommons.org/licenses/by/4.0/ | |
dc.subject | Fizik ve Fizik Mühendisliği | tr_TR |
dc.subject | Physics and Physics Engineering | en_US |
dc.subject | Kimya | tr_TR |
dc.subject | Chemistry | en_US |
dc.title | Magnetic and microwave properties of Ba- and Sr- hexaferrites prepared by solid state reaction route with boron addition | |
dc.title.alternative | Katı hal yöntemle sentezlenmi̇ş bor katkılı Ba- ve Sr- hekzaferri̇tlerin manyeti̇k ve mi̇krodalga özelli̇kleri̇ | |
dc.type | masterThesis | |
dc.date.updated | 2018-08-06 | |
dc.contributor.department | Biyo ve Nano Teknoloji Mühendisliği Ana Bilim Dalı | |
dc.identifier.yokid | 10084199 | |
dc.publisher.institute | Biyonano Teknoloji Enstitüsü | |
dc.publisher.university | FATİH ÜNİVERSİTESİ | |
dc.identifier.thesisid | 424469 | |
dc.description.pages | 94 | |
dc.publisher.discipline | Diğer |