Farklı yüzey hazırlama işlemlerinin zirkonya-indirekt kompozit rezin bağlanma dayanımına etkilerinin incelenmesi
dc.contributor.advisor | Tak, Önjen | |
dc.contributor.author | Güder, Zinde | |
dc.date.accessioned | 2020-12-29T12:15:47Z | |
dc.date.available | 2020-12-29T12:15:47Z | |
dc.date.submitted | 2016 | |
dc.date.issued | 2019-03-07 | |
dc.identifier.uri | https://acikbilim.yok.gov.tr/handle/20.500.12812/410193 | |
dc.description.abstract | Bu uzmanlık tezinin amacı farklı yüzey işlemlerinin zirkonya ile indirekt kompozit rezin materyalin makaslama bağlanma dayanımı üzerindeki etkilerinin incelenmesidir. Y-TZP zirkonya bloklardan (IPS e.max ZirCAD) elde edilen 100 adet örnek (15x12x2 mm) iki ana gruba ayrılarak kumlama veya ytterbium-doped fiber lazer ile pürüzlendirildi. Daha sonra her iki grup zirkonya primerlere göre beş alt gruba ayrıldı [Clearfil Ceramic Primer Plus (LC - KC), Monobond Plus (LM - KM), Signum Zirconia Bond (LS - KS), Z-Prime Plus (LZ - KZ) ve primer uygulaması yapılmayan (LP - KP)]. Yüzey uygulamaları sonrası bütün gruplara indirekt kompozit (Solidex) tepimi yapıldı ve örnekler üniversal test cihazında 0,5 mm/dk hızla makaslama testine tabi tutuldu. Elde edilen değerler student t-testi, iki yönlü varyans analizi ve Bonferroni çoklu karşılaştırma testleri kullanılarak istatistiksel olarak değerlendirildi. Lazer ile elde edilen Ra değerleri (1,23 ± 0,07 µm), kumlama ile elde edilen Ra değerlerinden (0,76 ± 0,05 µm) anlamlı derecede yüksek bulunmuştur (p<0,001). En yüksek ortalama makaslama bağlanma değerlerini LS (13,20 ± 1,72 MPa) ve LZ (13,45 ± 1,80 MPa) grupları gösterirken, KP (2,69 ± 0,82 MPa) grubu tüm diğer gruplardan daha düşük bağlanma değerleri göstermiştir (p<0,05). Bu çalışmanın sonuçlarına göre, lazer uygulaması, kumlamaya oranla daha yüksek bağlanma dayanımı elde edilmesini sağlarken, zirkonya primerler ile lazer uygulamasının kombine edilmesi makaslama bağlanma dayanımını anlamlı ölçüde arttırmıştır. | |
dc.description.abstract | The aim of this study is to evaluate the influence of different surface treatment methods on the shear bond strength of indirect composite resin material and zirconia. A hundered samples (15x12x2 mm) which were obtained from Y-TZP zirconia blocks (IPS e.max ZirCAD) assingned to two main groups and roughened by using air abrasion or Ytterbium-doped fiber laser. Each group were further divided into 5 primer subgroups [Clearfil Ceramic Primer Plus (LC - KC), Monobond Plus (LM - KM), Signum Zirconia Bond (LS - KS), Z-Prime Plus (LZ - KZ) and no primer application (LP - KP)]. After surface treatment indirect composite resin (Solidex) was applied to all groups and loaded in a universal testing device for shear bond stress with at a crosshead speed of 0,5 mm/min. Data obtained were analyzed statistically by student t-test, two-way ANOVA and Bonferroni multiple comparison test. The Ra values for laser group (1,23 ± 0,07 µm) were significantly higher than the Ra values for air abrasion group (0,76 ± 0,05 µm) (p<0,001). While the LS (13,20 ± 1,72 MPa) and LZ (13,45 ± 1,80MPa) groups showed the highest mean bond strength values, KP (2,69 ± 0,82 MPa) group showed the lowest shear bond strength values of all groups (p<0,05). Regarding the results of the present study; while laser application leads to higher shear bond strength values than air abrasion, combination of zirconia primers with laser application significantly increases shear bond strength | en_US |
dc.language | Turkish | |
dc.language.iso | tr | |
dc.rights | info:eu-repo/semantics/openAccess | |
dc.rights | Attribution 4.0 United States | tr_TR |
dc.rights.uri | https://creativecommons.org/licenses/by/4.0/ | |
dc.subject | Diş Hekimliği | tr_TR |
dc.subject | Dentistry | en_US |
dc.title | Farklı yüzey hazırlama işlemlerinin zirkonya-indirekt kompozit rezin bağlanma dayanımına etkilerinin incelenmesi | |
dc.title.alternative | Effect of different surface treatment methods on bond strenght of zirconia and indirect composite resin | |
dc.type | doctoralThesis | |
dc.date.updated | 2019-03-07 | |
dc.contributor.department | Protetik Diş Tedavisi Anabilim Dalı | |
dc.subject.ytm | Composite resins | |
dc.subject.ytm | Dental materials | |
dc.subject.ytm | Tooth surface | |
dc.subject.ytm | Surface roughness | |
dc.subject.ytm | Sanding | |
dc.subject.ytm | Dental stress analysis | |
dc.subject.ytm | Zirconium | |
dc.subject.ytm | Zirconium oxide | |
dc.subject.ytm | Lasers | |
dc.identifier.yokid | 10104330 | |
dc.publisher.institute | Diş Hekimliği Fakültesi | |
dc.publisher.university | KOCAELİ ÜNİVERSİTESİ | |
dc.type.sub | dentistThesis | |
dc.identifier.thesisid | 417202 | |
dc.description.pages | 116 | |
dc.publisher.discipline | Diğer |